In recent years, Mg alloys have great promise for weight-saving applications, because of their superior properties over monolithic metals, in the field of automotive and aerospace industries. In this study, the dry sliding wear behavior of Mg- SiC alloys with different sintering temperatures (375°C, 400°C, 425°C) were investigated. Mg with %10 weight SiC powders were mechanically mixed and alloyed and then fabricated successfully via fast heating under vacuumed argon atmosphere. The friction coefficient, hardness value, and wear resistance of the alloys were higher than those of the pure Mg. The increase in the sintering temperature of the Mg-SiC alloys up to 425°C caused an increase in the friction coefficient and a decrease in the wear mass loss respectively.
Son yıllarda, Mg alaşımları, otomotiv ve havacılık endüstrileri alanında, monolitik metallere göre üstün özellikleri nedeniyle, ağırlık tasarrufu sağlayan uygulamalar için büyük umut vaat etmektedir. Bu çalışmada, farklı sinterleme sıcaklıklarına (375°C, 400°C, 425°C, 450°C) sahip Mg-SiC alaşımlarının aşınma davranışları incelenmiştir. Ağırlıkça %10 SiC içeren Mg-SiC tozları mekanik olarak karıştırılıp alaşımlanmış ve ardından vakumlu argon atmosferi altında FAST ile sinterlenmiştir. Alaşımların sürtünme katsayısı, sertlik değeri ve aşınma direnci saf Mg'den daha yüksektir. Sinterleme sıcaklığının 425°C'ye kadar artması, Mg-SiC alaşımlarının sürtünme katsayısının artmasına ve aşınma kütlesi kaybının azalmasına neden olmuştur.
Download Article in PDF (575.2 kB)