Aheterogeneous catalyst in the form of Au nanoparticles (Au NPs) immobilized porous manganese oxide (Mn5O8) microspheres was synthesized. Mn5O8 microspheres were obtained by sol-gel templating method. The heterogeneous catalyst (Au@Mn5O8) showed good performance when compared with similar catalysts in the oxidation of benzyl alcohol (BnOH). Au@Mn5O8 microspheres obtained by the decoration of Au NPs on Mn5O8 microspheres performed 99.4% of BnOH conversion and 100 % of benzaldehyde (BnCHO) formation yield. Also the heterogeneous catalyst showed a good stability and agglomeration resistance in the reusability experiments. There was no remarkable loss in the catalytic activity when the catalyst was reused up to 5 times.
Altın nanopartiküllerle (Au NP’ler) dekore edilmiş gözenekli manganez oksit (Mn5O8) mikroküreleri formunda heterojen bir katalizör sentezlenmiştir. Mn5O8 mikrokürelerinin sentezi için sol-jel kalıplama yöntemi kullanılmıştır. Sentezlenen heterojen katalizör, benzil alkol (BnOH) oksidasyonunda benzer katalizörlerle karşılaştırıldığında iyi performans göstermiştir. Au NP’lerin Mn5O8 mikroküreleri üzerinde immobilizasyonu ile elde edilen heterojen katalizör (Au@Mn5O8) ile %99.4 BnOH dönüşümü ve %100 benzaldehit (BnCHO) oluşum verimi elde edilmiştir. Ayrıca heterojen katalizör, tekar kullanılabilirlik deneylerinde iyi bir stabilite ve aglomerasyona karşı direnç göstermiştir. Au@Mn5O8 mikroküreleri, katalitik aktivitede kayda değer bir kayıp olmaksızın 5 kata kadar yeniden kullanılabilmiştir.
Download Article in PDF (2.7 MB)