Nylon3 was prepared through base-catalayzed hydrogen transfer polymerization of acrylamide. The polymer was fully characterized by FTIR, FT-Raman, 1H-NMR, 13C-NMR, DSC, TGA, XRD, MALDI-MS, and end-group analyses. Glass transition temperature, thermal degradation temperature, d-space values, crystallinity, average molecular weights and polydispersity of nylon3 obtained were determined. Initiation, propagation and termination mechanisms of base-catalyzed hydrogen transfer polymerization of acrylamide were proposed using the structural analyses of nylon3 obtained.
Naylon3 akrilamitin baz katalizli hidrojen transfer polimerizasyonu ile hazırlandı. Polimer FTIR, FT-Raman, 1H-NMR, 13C-NMR, DSC, TGA, XRD, MALDI-MS ve uç grup analizleri ile tamamen karakterize edildi. Camsı geçiş sıcaklığı, termal bozunma sıcaklığı, kristal yüzdesi, d-boşluk değerleri, ortalama molekül kütlesi ve polidispersitesi belirlendi. Akrilamitin hidrojen transfer polimerizasyonunun başlama, büyüme ve sonlanma basamakları elde edilen naylon3 polimerinin yapısal analizi kullanılarak önerildi.
Download Article in PDF (552.5 kB)